在水泥或著是石灰砂漿中摻加進適當的摻合料，比如粉煤灰、硅藻土等等，以節約水泥或者是石灰用量，同時，改善一下砂漿的和易性。下面小編為大家介紹一下濟南抹面砂漿怎樣使用。

Appropriate admixtures such as fly ash and diatomite are added to the cement or lime mortar to save the cement or lime consumption and improve the workability of the mortar. The following editor will introduce how to use Jinan plastering mortar.

1、抹面砂漿基層處理將板底或混凝土、砌塊等抹灰面上的雜物清理干凈，對于鋼筋混凝土，應將混凝土上的突出物剔除，并將模板接縫處殘余的海綿條或膠帶紙等清理干凈。將基底上浮塵掃除，提前用水噴淋，使之濕潤。同時應對施工部位的樓地面進行清掃，以利于抹灰后清理抹灰時產生的落地保溫砂漿。

1. Plastering mortar base course treatment: clean the sundries on the bottom of the slab or the plastering surface of concrete and blocks. For reinforced concrete, remove the protrusions on the concrete, and clean the residual sponge strips or adhesive tapes at the formwork joints. Remove the floating dust on the base and spray it with water in advance to make it wet. At the same time, the floor of the construction site shall be cleaned to facilitate the cleaning of the floor insulation mortar generated during plastering after plastering.

2、涂大旗界面劑或用拉毛在涂抹處理干凈的基層上滿涂界面劑或用拉毛，沿鋼筋混凝土與加氣混凝土接縫處抹3-4mm厚抹面砂漿，隨即壓入400寬耐堿網格布每邊200寬，表面在用抹面砂漿抹平。然后滿涂界劑或用拉毛。

2. Apply the big flag interface agent or roughen the surface of the cleaned base layer with the interface agent or roughen it. Apply 3-4mm thick plastering mortar along the joint between the reinforced concrete and the aerated concrete. Then press the 400 wide alkali resistant mesh cloth with a width of 200 on each side. The surface is plastered with the plastering mortar. Then apply the coating agent or roughen it.

3、抹面砂漿貼餅厚度控制點采用保溫砂漿設置，大小為20*20，厚度為所需保溫層厚度，保溫層厚度控制點間距宜為1.5m以內。

3. The thickness control point of plastering mortar paste is set with thermal insulation mortar, with the size of 20 * 20 and the thickness of the required thermal insulation layer. The distance between the control points of thermal insulation layer thickness should be within 1.5m.

4、保溫砂漿分層涂抹

4. Thermal insulation mortar layer by layer

(1)拌料：用人工按保溫砂漿：水=1：1(重)攪拌均勻成膏狀，根據氣候溫度可自行掌握和易性，隨拌隨用。

(1) Mixing materials: manually mix the thermal insulation mortar: water = 1:1 (weight) to form a paste. According to the climate and temperature, the workability can be controlled by yourself, and the mixture can be used at any time.

(2)涂抹層保溫砂漿。要求厚度不得高過1.5cm，壓實，表面留毛面。

(2) Apply thermal insulation mortar. It is required that the thickness shall not be more than 1.5cm, and it shall be compacted with rough surface left on the surface.

(3)二層形成初凝后(加鋼絲網)，涂抹第三層，厚度不高過2cm。注意：下一層涂抹一般間隔24，分層之間留毛面。

(3) After the initial setting of the second layer is formed (steel wire mesh is added), the third layer shall be coated with a thickness of no more than 2cm. Note: the next layer is generally applied at an interval of 24, leaving a rough surface between layers.

(4)抹面砂漿分層涂抹時，應適度按壓，以確保層與層之間能形成有.效粘結，但不可在同一部位來回抹壓。在涂抹中，發現有鼓包產生，應及時剔除補抹。抹面砂漿

(4) When the plastering mortar is applied in layers, it shall be pressed moderately to ensure that there is a gap between layers Effective bonding, but cannot be plastered and pressed back and forth at the same position. In case of any bulge during coating, it shall be removed and repaired in time. Plastering mortar

5、鋪設耐堿玻纖網布

5. Laying alkali resistant glass fiber mesh

保溫砂漿表面收光時，把耐堿玻纖網布用抹子直接壓在材料表面，同時收光，嚴禁漏鋪。耐堿玻纖網布鋪設時要求平整、無皺褶，順序搭接，搭接寬度30-50mm;外檐鋪設時搭接寬度80-100mm;陽角與保溫接茬處壓貼100mm寬的耐堿玻纖網布。

When the surface of thermal insulation mortar is polished, the alkali resistant glass fiber mesh cloth shall be directly pressed on the material surface with a trowel, and the surface shall be polished at the same time. It is strictly prohibited to omit laying. The alkali resistant glass fiber mesh cloth shall be laid flat and without wrinkles, and shall be overlapped in sequence, with the overlapping width of 30-50mm; When laying the outer eaves, the overlapping width is 80-100mm; 100mm wide alkali resistant glass fiber mesh cloth shall be pressed and pasted at the external corner and insulation joint.

注意：當施工期間，氣溫超過30℃的時候，要在拌完成之后的3小時里面使用完畢。為了方便配料，也為了減少施工中的切鋸工作量，在建筑施工中，要進行排塊的設計。更多相關事項就來我們網站http://www.man5g.cn咨詢了解吧！

Note: when the temperature exceeds 30 ℃ during construction, it shall be used within 3 hours after mixing. In order to facilitate batching and reduce the workload of cutting and sawing during construction, the design of block arrangement shall be carried out during construction. For more information, please visit our website http://www.man5g.cn Consult and understand!